    I'm hoping that this short will help alleviate some of the initial difficulties I have faced while working with plastics. I was fortunate enough to experiment with only scrap, but I've heard from a number of people who managed to destroy sheets that they paid good money for. These are the most frequently asked questions I see on a variety of forums and I will answer them as best I can. If you have any specific or complicated questions that I cannot answer directly, I recommend contacting a local plastics shop.

    Materials

    ABS (Pure, not ABS/PVC blend)
    Desciption: Tough and impact-resistant, this material works well for protective applications such as small appliance housings. Commonly used to make hard-sided luggage and is the standard material choice for plastic injection moulding (and therefore) it's what most of the plastic parts in your computer are made out of.
    Highest operating temperature: 100+ F to 200+ F
    Tooling behavior: Heats and melts very quickly above 125F. Use Slowest speeds possible with medium tooth count. Easy to carve with standard hand tools.
    Avoid: Abrasive cutting tools or anything that creates excessive friction. Will fume excessively if heated so wear a filtration mask when cutting.
    Commonly Available Colors: Black, Brown, Beige

    PVC & CPVC
    Description: Low cost and ease of availability. Extremely high chemical and moisture resistance and very good impact resistance. However it mars fairly easily under abrasion and has comparatively poor tensile strength.
    Highest operating temperature: 100+ F to 200+ F (300F for CPVC)
    Tooling behavior: Provided the right blades are used, PVC can be as easy to work with as medium density natural woods. Behaves similarly to polycarbonate, but can be much more aromatic (smelly) due to its lower maximum operating temperatures.
    Commonly Available Colors: Grey, White, Clear (expensive)

    Polyethylene
    Description: Coming in a very wide variety of material densities this plastic is the most commonly used plastic in product manufacturing due its low cost and ease of injection moulding as well as recycling properties. Resists abrasion very well but has sub-par ability when it comes to structural rigidity and won't withstand much flexing.
    Highest operating temperature: 100+ F to 200+ F (300F for CPVC)
    Tooling behavior: Usually not desirable because it can become dimensionally unstable at lower temperatures, and melts excessively when being cut.

    Polycarbonate
    Description: Offers impact strength over a wide temperature range. Use indoors and outdoors. Offers a superior ability to resist being torn apart. They generally can withstand a pulling force greater than 10,000 psi. Has a greater ability to withstand a forceful sudden impact, similar to being struck by a hammer. Products listed with high impact strength generally can withstand 5 foot-pounds of energy per inch of thickness under normal conditions.
    [​IMG]
    Highest operating temperature: 200+ F to 300+ F
    Tooling Behavior: Shreds into fine pieces when the correct blades are used and it very receptive to tooling. Has a very low tendency to melt under friction, unless the wrong blade type is used when cutting it. Flexes easily and accepts high pressure amounts. Very easy to tap and drill. Machining experience comparable to aluminum in most circumstances.
    Commonly Available colors: Clear, Opaque Black, White Tint, Grey Tint, Bronze Tint, Black Tint, UV resistant Black Tint (used for public transportation applications)

    Polyester (PETG)
    Highest operating temperature: 100+F to 150+F
    Description: Extremely low cost Polycarbonate substitute material, but is considerably softer and therefore has lower abrasion resistance. Optical clarity is also lower.
    Tooling Behavior: Can be temperamental in that it can cut a little bit too easily at times. Feels vaguely similar to wax and caution is needed to avoid overheating the sheets as they will become quite sticky against blades inducing friction. Generally pest to avoid this material if you need to cut out any complex or intricate shapes due to that property.

    Polypropylene
    Description: Most commonly used plastic across a wide variety of applications due to its low cost. It has a hard, smooth chemically resistant surface. Is non-toxic. Commonly used for pipes, valves, and fittings.
    Highest operating temperature: 100+ F to 200+ F
    Tooling Behavior: Heats and melts very quickly above 125F. Use Slowest speeds possible with medium tooth count. Easy to carve with standard hand tools but can discolor under pressure.
    Avoid: Abrasive cutting tools or anything that creates excessive friction.
    Commonly Available Colors: Black, Brown, White, Translucent White

    Acetal (Delrin): An exemplary high density plastic that is and almost perfect aluminum substitute. Dimensionally stable, high tensile strength, wear resistant, and fairly impact resistant. Comonly used to make bearings, pulleys, and wheels. Only downside is comparatively high cost (mainly due to high density).
    Tooling Behavior: Shreds into fine pieces when the correct blades are used and it very receptive to tooling. Has a very low tendency to melt under friction, unless the wrong blade type is used when cutting it. Flexes easily and accepts high pressure amounts. Very easy to tap and drill. Machining experience comparable to aluminum in most circumstances.
    Commonly Available colors: Opaque Black and White

    Acrylic (Cast)
    Description: Moderate tensile strength material with good abrasion resistance qualities. Has low impact resistance and a tendency to split or crack under sheering forces. Optimal material in applications that involve heat-warping.
    Highest operating temperature: 150+ F to 250+ F
    Tooling Behavior: Better friction tolerances than ABS or Polypropylene, but will melt fairly quickly under friction. Can be very picky about blade types and lower blade speeds will need to be used. Much be worked with in a similar manner to balsa wood due its semi-brittle nature.
    Avoid: Abrasive cutting tools or anything that creates excessive friction. Will fume moderately when heated so wear a filtration mask when cutting.
    Commonly Available Colors: Clear, Opaque (White, Grey, Black, Red, Yellow, Blue, Green), Solid Tints (White, Grey, Bronze, Red, Blue, Green, Yellow, Amber), Fluorescent/UV Tints (Amber, Red, Green, and Blue)

    Acrylic (Extruded)
    Description: Often used to replace glass, provides outstanding optical clarity even at greater thicknesses. Has a smooth surface for use as windows and signs, but is less impact resistant than polycarbonate. Higher potential for fume production and more brittle than cast acrylic. Difficult to machine and has an even higher tendency to split or crack under sheering forces than cast acrylic. Most often seen in the form of bars, rods, tubes, balls, and discs.
    Highest operating temperature: 150+ F to 250+ F (Does melt faster than Cast Acrylic due to its higher molecular density)
    Tooling Behavior: Better friction tolerances than ABS or Polypropylene, but will melt fairly quickly under friction. Can be very picky about blade types and lower blade speeds will need to be used. Much be worked with in a similar manner to balsa wood due its brittle nature. Extruded Acrylic is slightly more fragile than Cast Acrylic and is therefore harder to work with.
    Avoid: Abrasive cutting tools or anything that creates excessive friction. Will fume moderately to excessively(depends on the brand) when heated so wear a filtration mask when cutting.
    Commonly Available Colors: Clear

    Recommended Tools

    ScrollSaw: Ideal for detail work and causes MUCH less friction that other reciprocating blade tools. Could ideally be used for the majority of cutting work that doesn't involve precise 90-degree measurement cuts. CAN be used for interior plunge cutting if a 11/16th to 1/4 inch pilot hole is drilled into the material. The blade than be untensioned and fed through the pilot hole.

    TableSaw: In order to work with plastics you will need to purchase and use an OSB/Plywood blade (200 teeth) to prevent from cracking/splitting your sheets, which can lead to shrapnel. Higher bite angles work better for most plastics.

    BandSaw: Fairly good tool for cutting plastics without splitting, or cracking sheets. Can melt extruded acrylic very quicky if setup improperly. Also one of the easiest tools to control the resulting mess from because all of the shaving come directly out of the bottom. DO NOT buy a new bandsaw that's cheaper than $125. These have alot of moving parts, so unless you can find an industrial-grade bandsaw at an estate or garage sale it's best to buy a quality name brand unit. Cheaper models may be finicky however and this is a very difficult tool to properly calibrate and maintain. So if you have a limited budget and little experience it may be best to opt for a TableSaw instead.

    Jigsaw: A fairly good substitute for a ScrollSaw, especially when used for interior/detail cutting or sheet trimming. Much more predictable and variable for plastic cutting than a rotary tool. Use metal smooth-cut (24tpi) blades for most cutting. For smaller cuts or low heat tolerance materials scroll-cut wood blades (10tpi upcut/downcut) are recommended. Mine is setup upside-down and attached to a shelfboard to allow me to cut sheets without having to back them with plywood (which I recommend for normal jigsaw operation but can be difficult to setup safely).
    [​IMG]

    DrillPress: Far more controllable and precise than a hand power drill. Will allow you to use spade bits for larger holes as well as help you control your downforce.
    Drill Bit Set: for holes smaller than 1/4" any drill bit set seems to work fine. But for larger hole diameters a plastic specific set or a good variety of spade bits is essential. I prefer using spade bits over hole saws or larger drill bits if I'm working with plastics (except for ABS and polypropylene which get "gummy" when spade bits are used).
    Low grit count rotary sanding bits: These are very useful for shaping and smoothing out plastic sheet edges with either a rotary tool or a drillpress.

    Hack Saw (or miter saw): While not at all usable with acrylic a hacksaw works really well with ABS, polyethylene, and thinner sheets of polycarbonate. I don't use these very often so I'm not sure which tooth counts will work best, but wood blades seem to work just fine.

    Rotary Tool: While you can most likely do without this tool entirely, it's perfect for smaller shaping and etching tasks. It's not very useful for cutting most plastics though. To avoid excessive melting or blade sticking it's best to use high-speed cutting bits. Abrasive bits will not work properly with most plastic materials.

    Needle Files: A triangular needle file works best for flat surfaces and a round one is great for curves. Bot are used for cleaning the edges of sheet after initial cutting, and before sanding them to a finished edge.

    X-acto knifes: These can be use to carve softer plastics or use the dull side to deburr cut edges of plastic sheets. A good variety of blade shapes and lengths is recommended.

    Deburring Tool: This is a thick handles pen looking too with a curved swivel blade on the end. It's made solely for deburring the edges of cut holes and can make quick work of cleaning up rounded edges and drilled holes. They can be difficult to find because they are machining tools and not woodworking tools so don't expect to find these are Home Depot or Lowe's. Mcmaster.com or Sears are the best places to look.

    Heat gun (30w minimum): USE THIS WITH LEATHER WORK GLOVES, PLIERS, AND A FILTER MASK. This tool is extremely useful and allows you to heat-warp Acrylic and lower thicknesses of Polycarbonate. Must be used outdoors since sheets can leech fumes and the tool itself can be a fire hazard. You have to be careful with it though, and refusing to wear protective gloves will lead to injury. Hot plastic gets tacky and will stick to skin or burn you really quickly. Nevermind that you're also working with a tool that operates above 350F. DO NOT USE GLOVES THAT ARE NOT LEATHER or otherwise unrated as fireproof.

    Strip Heater: USE THIS WITH LEATHER WORK GLOVES, PLIERS, AND A FILTER MASK. For long straight heat-warping bends this is the ideal tool. It can heat a wide area evenly and at a more predictable temperature then a heat gun.

    Sandpaper (250 to 1000 grit): If you want finished edges, this will be the most effective method. Flame polishing is a difficult method to perfect and will only work with acrylic so I don't recommend it unless you have a stockpile of scrap to practice on first. When sanding plastic you don't have to progress as slowly as you would when sanding metal, so you may only need 3 sheets (400g, 800g, and 1000g) to get glossy edges.

    IPS Weld-on #3 or #4: This is an extremely useful and effective plastic solvent that fuses ABS, Polycarbonate, and Acrylic together (in any pure combination of the three). Simple brush onto or apply to contact area with syringe then secure pieces together in the final form you want. #3 formula is slightly thicker and faster setting, while #4 is water-thin and sets more securely. #4 is recommended for anything you are trying to make air-tight because it's thin enough to use capillary action to fill all of the gaps between the sheets you are joining together. In order to join sheet edges securely and tightly make sure they are sanded to atleast 400grit level and are straight enough to make a scure bond. You do not have to apply any contact pressure to get a good chemical bond. Over application will lead to ugly, but working joints. Can be applied an reapplied as needed without complications.
    It's a good idea to use this in a ventilated area, and while it will not adhere your skin to plastic it WILL create permanent fingerprints. This is a mildly toxic substances so excessive skin contact is not a good idea.
    It with also work with butyrates and styrenes, but I have not tested it on polypropylene or polyethylene yet so you'll need to ask a plastics shop about compatability. I do know that it is completely incompatible with all PVC plastic blends so avoid buying ABS/PVC (Kydex T). ABS/PVC is a crappy plastic anyways. If you need a specific solvent for a material, check out the wide range of products available from IPS: http://www.ipscorp.com
    Both #3 and #4 (and a whole host of other plastic adhesives) are available from McMaster (page 3229).
    To apply Weld-on accurately and safely I recommend using 3ml luer-lock syringes with flexible PTFE tubing "needles".
    These can be purchased from medical supply, or through industrial supply catalogs such as McMaster (part #s 7510A651 & 75175A691)

    Swimming goggles or safety glasses: For the most part plastic isn't dangerous to work with since the particulates create from cutting are low weight and low velocity so impact resistance is less of a concern. However, goggles are vital for protecting your eyes from dust and shavings while tooling or sanding. Regular safety glasses will work fine.

    Water-jet cutting: Yeah, I wish I had access to this frequently too. Water-jet cutting will work just fine with all of the above listed plastics provided you don't make your design with too many small poorly supported pieces. Polycarbonate can withstand lots of stress while having some extremely small pieces left after cutting, but with ABS and Acrylic any pieces that are connected with joints thinner than 9/16 will probably snap off in the process of cutting.

    Machining Plastics
    Plastics are quite temperamental when it comes to machining. Only certain tools can cut them safely and reliably and you have to work at a pace of patience or you'll end up ruining your sheets. Or even worse, getting yourself injured. Out of all the available materials in this category, polycarbonate is by far the most forgiving. So if you have no previous experience working with plastic, or you have limited access to tools, it would be a good idea to consider using only polycarbonate in your project.
    Before working with plastic you also have to take into account blade speed, friction, bite angle, tooth-counts, fume production, and pressure. For tool recommendations see above, but the general rule of thumb is work slow, and work with as little force as possible. Especially if you're working with brittle plastics.

    When Cutting: Feed slowly, avoid friction, avoid side-forces, use the right blade. Slow down or stop if melting starts. Allowing melting to continue may eventually allow the blade to yank your work out of your hands, or it could simply ruin your power tool. Plus, metling also leads to fumes, and those can give you the nastiest headaches you've ever experienced in your life.

    When Drilling: Use slow to medium speed and only slight downward pressure. Optimally the drilling process should sound like waves on a beach or sandpaper rubbed on metal. Make sure to clean your drillbit off after drilling each hole (the heat gun is also extremely useful for this). For drilling holes 1/4-inch or larger use spade bits or bits made specifically for plastics. Plastic specific drill bits have a shallow bite angle to prevent the drill bit from digging into the plastic and therefore getting stuck and biting a piece of your sheet off in the process. If you're going to be working with plastic quite frequently, a plastic specific drill bit set will save you alot of time and frustration.

    When Milling or Lathing: Follow speed and feed rate guidelines. For a decently comprehensive list see: http://www.boedeker.com/fabtip.htm
    Clearing swarf away from the part is vital so an ample supply of compressed air or coolant is important.

    When Lasercutting: Most machine shops will not be willing to cut plastic with lasercutting equipment because the equipment has to be setup specifically for plastics. Namely the power level has to be dropped WAY down and the focusing changed. Lasercutting plastic also will also require that your cuts take into account the effect radius of the laser, since it will cause secondary material loss outside of the beam area (up to an 0.0011" radius).
    Fume production is also a secondary problem that has to be taken into consideration when cutting any plastic other than acrylic.

    When Sanding: Plastic is as easy to sand (or more-so) as more soft crafting woods like balsa. Lower heat tolerance plastic melt wuickly though, so if you use power sanding tools (again) low speeds will be the most effective. When sanding with power tools the powder that comes off is heavy, but can stick to everything and get everywhere so you will need to wear a filter mask and goggles. Manual sanding isn't as messy so unless you sneeze a filter mask and goggles won't be required. I found that the more brittle the plastic, the more likely it is to produce razor-sharp edges when filed or sanded at angles. So if you are jointing pieces at corners or mitering sheets it's a good idea to wear gloves when sanding such pieces.
     
    Last edited: 3 Mar 2007
    rwb97, Nutman and lenne0815 like this.
  2. Captain Slug

    Captain Slug Infinite Patience

    Joined:
    25 Nov 2001
    Posts:
    1,403
    Likes Received:
    7
    When Tapping: Excluding Acrylic, drilled holes in plastics are very very easy to thread with even the cheapest tapping set. Here are the drill bit sizes you need to drill pass-through holes for mounting and holes to tap for the standard screw sizes.

    M3 (Machine screw used primarily for optical drives)
    Pass-through: 1/8-inch
    Tap: 3/32"

    #6 gauge 32 thread count (UNC #6-32 Common case screw)
    Pass-through: 9/64-inch for closest tolerance or 5/32-inch
    Tap: 7/64-inch

    Acrylic can be finicky to tap, especially extruded acrylic. Shallow threaded holes are fairly easy, but anything deeper than 1/4" becomes difficult. You have to go slow and if its start resisting, forcing it will lead to fractures or splitting. With acrylic it may help slightly to use a heat gun while tapping a hole.
    The rest of the plastics listed above however are very easy to tap and shread easily making way for the tapping head.

    Raw Plastic Material Shopping Sources
    1. CHECK YOUR LOCAL PHONE BOOK. Plastics shops and signmaking shops 9-times-out-of-10 will be selling their scrap plastic for a few dollars per pound. For some materials and tints you can buy whatever you need for 75% to 90% off warehouse or industrial pricing. Obscure items will obviously be hard to come by but you can save alot of money if you just look locally first.

    2. http://www.mcmaster.com

    3. http://www.usplastics.com

    4. http://www.tapplastics.com

    5. Many other online stores. I haven't checked other regions but I can try to find them if anyone asks.


    That covers most of what I've seen asked several dozen times. If there's anything you'd like to see added or questions you have feel free to contribute.

    Making precise machining templates
    (with a cheap inkjet printer.)

    One of the more irritating hurdles to making your plan become a reality involves converting your plan to actual dimensions to work from on your raw materials. I used to do this markup process using a mechanical pencil and a schematic to work from. This took alot of time and only produced precise results part of the time (due to scribing errors). Machinists use scribing all the time, but they have far more accurate measuring tools than I have at my disposal.
    After a recent project I realized I could use my printed to eliminate the need for scribing measurements on my part. This method is meant for any part that is 10" x 8" or smaller. Anything larger and you will have to combine sheets or find a local print shop that can print much larger labels or decals.

    Software
    There are so many options for software, and most of the more common titles cost more than the average person can afford. I've tried every free trial there is available and I've found one to be the easiest to learn and the most useful since it's an unlimited free trial.
    Alibre Xpress is the free version of the full package and will allow you to design simple assemblies and part templates for whatever use you want. It's configured similarly to other Solid CAD programs in that you simply make a sketch on a plane then use one of several methods to extrude the sketch into a solid shape.

    Step One: Measure & Sketch
    Obviously if you're going to make a part you need measurements to work from. Whatever part you're making Alibre will allow you to sketch in the details you want. For hole placements relative to a corner simply start a line from the center (x0y0z0) by clicking there and then right click and select "Direct Coordinate Entry" which will allow you to place the other end of the line relative to the start of it.
    Just continue sketching until you have a finished part.
    [​IMG]
    Step Two: PrntScrn
    Screen capture the sketch from Alibre with the sketching grid turned off. In a graphics program paste the screen shot and crop the image around the sketch. Select only the sketch lines and sketch nodes and copy then paste into a new image. Use brightness/contrast to turn the sketch black and then flatten the image.
    Step Three: Page layout & Printing
    Save as a temporary image and load as Clip Art from File (or just paste) in Microsoft Word (or similar suite). Right click the image and select properties to change the image dimensions to match the dimensions of the sketch in Alibre.
    [​IMG]
    For smaller parts you can fit multiple sketches on a single page. It may also help to save your sketch images as .PNG files with an Alpha Channel layer. That image type seems to scale more cleanly in Microsoft Word for some reason.
    Put one full-sheet label in the printer face down and then print your template page.
    [​IMG]
    Step Four: Application
    Now simply use some sharp scissors to cut out your individual cutting template labels and apply them to your sheets. It's best to apply them onto the protective film that comes on the sheet because cleaning the label adhesive off of the sheet after doing all of your cutting and drilling can be a time-consuming process.
    [​IMG]
    Step Five: Assembly
    Now that all of your individual parts are cut and drilled you can put them together as planned using whatever method you intended.
    [​IMG]
     
    Last edited: 3 Mar 2007
    Nanosec likes this.
  3. mobius9

    mobius9 Minimodder

    Joined:
    4 May 2004
    Posts:
    348
    Likes Received:
    0
    excellent guide. I'll be using this in the future :)
     
  4. advance

    advance What's a Dremel?

    Joined:
    18 Apr 2005
    Posts:
    91
    Likes Received:
    0
    Same with me...

    *Adds to bookmarks.
     
  5. Ghlargh

    Ghlargh What's a Dremel?

    Joined:
    16 Nov 2003
    Posts:
    276
    Likes Received:
    0
    I have found that you can actually use a high speed cutting blade for many clear acrylic sheets (plexiglass windows) because allmost all of the heat goes out with the parts that are ground off.

    Especially brand name plexiglass where no melting occours even with a dremel and a cutting disc at 30 000 RPM, Lower quality acrylics will melt more, but all i get is a little crap that sticks to the edges and can easily be removed with a finger. You will however need to have the protective plastic foil on while cutting. if your acrylic comes without protective plastic foil, use masking tape. larger areas can be covered in paper or cloth to avoid using epic ammounts of masking tape.

    for shaping, i go one round with a coarse grit 1/2" sanding drum for Dremel at 30 000 RPM and press all i want, when i'm satisfied with the shape i go one round pressing softly to remove all splattered plastic.
    Then i fine sand with a medium fine 1/2" drum at 10 000 RPM, pressing very softly.

    This usually gets me a very nice resuly, especially when i need rounded edges and round shapes.

    However, for straight lines, i reccomend a hand held jigsaw or band saw, it's simply hard to make a smooth straight cut with a Dremel.
    For smoothing a straight edge, just use a coarse metal file or a fine wood file (about the same coarsness).
     
  6. Captain Slug

    Captain Slug Infinite Patience

    Joined:
    25 Nov 2001
    Posts:
    1,403
    Likes Received:
    7
    The "problem" I have with high speed tools with plastic is the fume production. And if you use high speeds with toothed blades the melting excess will eventually grab ahold of the blade.

    A dremel may work under some circumstances. But I will never specifically recommend it for anything other than small detail work and edge finishing.
     
  7. ConKbot of Doom

    ConKbot of Doom Minimodder

    Joined:
    2 Jul 2003
    Posts:
    2,160
    Likes Received:
    6
    From what Ive seen of it, Lexan/Polycarbonate works pretty much like clear metal... Drilling large holes in it can be a bit of a pain, especially with small work pieces. Definitely use a hole saw or similar rather then something like a 5/8" drill bit meant for metal if you need a 5/8 hole".

    Thin lexan can be creased/bent while cold, its just that large radii may give difficulty and may need heating. It may not be this way for other plastics, but if you don't have the *exact* correct bit/blade for it, dont stress out too much. If it'll work for aluminum, it should work for lexan. The only real difference is that lexan is more "gummy" than aluminum, and tends to make long strands when you turn/drill it, so like I said above, when it comes to large holes, large drill bits may not work that well.
     
  8. Captain Slug

    Captain Slug Infinite Patience

    Joined:
    25 Nov 2001
    Posts:
    1,403
    Likes Received:
    7
    Definitely. Polycarbonate shreds much like the softest alloys of aluminum. I prefer to not use holesaws with either if I can help it because spade bits work more predictably with it and won't get stuck or bite into the edges. If you do use a holesaw it's best to use one with a drillpress and a wood spacer clamped to the underside of your sheet.

    Oh, and one thing I forgot to note in the guide. You can polish the edges of polycarbonate sheets with nothing more than friction. So if you don't have any sandpaper, put Hex socket bit into your power drill or drillpress and run it along the edges of the sheet for an edge similar to what you would get with 600grit sandpaper.
     
  9. BBurger

    BBurger What's a Dremel?

    Joined:
    7 Apr 2005
    Posts:
    155
    Likes Received:
    0
    Thanks for this guide! I've been playing around with a scrap piece of acrylic - never used the stuff before.

    Going to bookmark this for when I get more into acrylic stuff.
     
  10. Ghlargh

    Ghlargh What's a Dremel?

    Joined:
    16 Nov 2003
    Posts:
    276
    Likes Received:
    0
    As for fumes, i use a gasmask as combined eye protection and dust filter.

    Even if i have used up the filter's active carbon, the particle filter should take care of most crap i can produce with a dremel.
     
  11. mobius9

    mobius9 Minimodder

    Joined:
    4 May 2004
    Posts:
    348
    Likes Received:
    0
    how hazardous are the fumes? because I've done like 4 projects that involve a lot of cutting of acrylic and never worn a mask. :blah:
     
  12. Captain Slug

    Captain Slug Infinite Patience

    Joined:
    25 Nov 2001
    Posts:
    1,403
    Likes Received:
    7
    Not seriously, and you have to go above 250F when tooling it to get enough fumes to get a headache. Prolonged exposure is dangerous, and the potency (as far as headache production) will depend on the kind of acrylic you're working with. The really cheap and brittle stuff like the kind you can get at home depot is the absolute best at producing instant migraines and lingering smells.

    Just work the right kind of blades and avoid excessive tooling friction. And when sanding, no matter what you're working with you should be wearing a filter mask and goggles.
     
  13. sirbogey

    sirbogey What's a Dremel?

    Joined:
    7 Jun 2005
    Posts:
    23
    Likes Received:
    0
    Great guide for all modding neophytes like me! thanks for sharing
     
  14. Captain Slug

    Captain Slug Infinite Patience

    Joined:
    25 Nov 2001
    Posts:
    1,403
    Likes Received:
    7
    Update:
    I have slowly discovered that safety goggles are useless for protecting eyes from plastic dust, which is easily made airborne and can find it's way through the "breathing" holes in standard safety goggles. I have since switched over to swimming goggles because impact resistance is not a concern, and as a result have had no problems with plastic dust getting in my eyes.
     
    Shadow703793 likes this.
  15. HAXOR

    HAXOR Minimodder

    Joined:
    14 Oct 2003
    Posts:
    148
    Likes Received:
    0
    Slug, you're everywhere arn't you? :D


    Looks like a nice guide though, I haven't had any issues with plastic dust yet though, since I use that shopsmith bandsaw setup. If I do though, I'll be sure to try the swimming goggles.

    Hole saws are nasty with arcylics and lexan. Whenever I use it, it seems to tear apart the outside edges of the hole, so I've switched to just using a dremel and a sanding drum.

    BTW, I'm Celeron_Phreak from the OCForums. :)
     
  16. Captain Slug

    Captain Slug Infinite Patience

    Joined:
    25 Nov 2001
    Posts:
    1,403
    Likes Received:
    7
    Hence why band saws are the primary cutting tool in plastics shops. They only produce shavings and are of little concern when it comes to dust production. Just MAKE SURE you wear swimming goggles when sanding any kind of plastic.

    And I prefer using spade bits over hole saws when it comes to polycarbonate. For holes larger than 2 inches in diameter it'se best to just use a cutting tool of some kind (I use a shelfboard-mounted jigsaw).

    Or if you have a drillpress that will let you do so, sometimes running the holesaw in reverse will actually work.
     
  17. ArmyAnt

    ArmyAnt What's a Dremel?

    Joined:
    6 May 2004
    Posts:
    265
    Likes Received:
    0
    Slight rerror in extruded acrylic, you kept comparing it to extruded acrylic, like "is more brittle than extruded acrylic" while that is what it was talking about.
     
  18. MrWillyWonka

    MrWillyWonka Chocolate computers galore!

    Joined:
    25 Jul 2004
    Posts:
    5,892
    Likes Received:
    12
    Good guide! Thanks for the info on finished edges, should help with my mod!

    One thing you should add, when drilling plastic on a piece of wood, make sure that there are no old drill holes under the area of plastic you are drilling as this will often result is damaged edges or cracked plastic!
     
  19. Captain Slug

    Captain Slug Infinite Patience

    Joined:
    25 Nov 2001
    Posts:
    1,403
    Likes Received:
    7
    Added ScrollSaw and Swimming Goggles to tool list and amended Jigsaw, Bandsaw, and IPS Weld-On entries.
     
    Last edited: 12 Oct 2005
  20. Lemur 6

    Lemur 6 What's a Dremel?

    Joined:
    15 Mar 2005
    Posts:
    121
    Likes Received:
    0
    You forgot a few things

    There's one thing that cuts 1/4" and thinner sheets of acrylic like nothing else... a laser cutter. You can cut the most complex of shapes in minimal time. It's just like using a printer. You can even laser engrave aluminum, or even cut aluminum and steel with high powered industrial strength laser cutters (but those are rare and expensive).

    Do NOT cut polycarbonate or abs plastic in a laser cutter though, or you will generate some pretty toxic fumes :nono: (won't only give you a headache, but will endanger your life and others around you).

    Also, do realize that a laser cutter (or water jet cutters, or any other "beam" type cutters, i.e. plasma cutters) does not leave perfectly square edges. The edges will be slightly beveled depending on how the focusing was done.

    Also, some plastics were not mentioned. Nylon and Delrin are both nice plastics to work with in terms of machining. Delrin is just perfect plastic for machinability, strength, and chemical resistance (but comes at a price). Black delrin parts are just drop dead sexy. PVC is also good. It's fairly strong and machines fairly well.

    If you're having problems getting well polished edges and cracked holes with acrylic, flame polishing with a blow torch will work very well (again don't do this with polycarbonate, toxic fumes). Flame polishing holes reduces many of the surface imperfections that can initiate crack propagation, and gets perfect polished surfaces with minimal time and effort. Some practice is needed to get good even surfaces and it only works with small surfaces or edges.

    -Lemur 6
     